A Pilot-Plant Investigation of Factors Affecting Low-Temperature Corrosion in Oil-Fired Boilers

[+] Author and Article Information
R. C. Attig, P. Sedor

The Babcock & Wilcox Company, Research Center, Alliance, Ohio

J. Eng. Power 87(2), 197-202 (Apr 01, 1965) (6 pages) doi:10.1115/1.3678167 History: Received April 17, 1964; Online January 10, 2012


Methods for controlling or eliminating low-temperature corrosion are continually being sought to improve boiler availability and thermal efficiency. A small pilot plant was constructed at the authors’ company in which factors that affect low-temperature corrosion could be studied under closely controlled conditions. Results of tests on this unit show that: (a) The corrosion rate on carbon steel increases gradually as metal temperature falls below the acid dewpoint, passing through a peak at a metal temperature about 200 F. The corrosion rate then decreases as metal temperature continues to fall but begins to rise rapidly to extremely high values at temperatures just above the water dewpoint (⋍ 120 F). (b) Low-temperature corrosion of carbon steel can be practically eliminated if a method can be found for reducing the sulfur content of oil to about 0.5 percent. (c) The application of low-excess-air operation has the potential of eliminating low-temperature corrosion in boiler plants firing high-sulfur residual oils. (d) Corrosion of carbon steel above approximately 170 F can be reduced 30 percent or more by recirculating 25 percent of the flue gases to the burner. Future work will include a study of the effect of low-excess-air operation on high-temperature oil-ash corrosion and deposition and on the effect of oil ash on low-temperature corrosion.

Copyright © 1965 by ASME
Your Session has timed out. Please sign back in to continue.





Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In