The effect of density (relative densities 0.33 to 0.90) on the impact behavior of microcellular polycarbonate (PC) was investigated. Cell size and foaming gas content were also considered. Flexed-beam Izod impact tests were conducted and the impact strength of these foams appears to be a strong function of both density and cell size. The impact strength was observed to improve over the unprocessed polycarbonate’s impact strength for foams with relative densities of 60 percent and above. In terms of cell size, the impact strength increased with increasing cell size at a given density.
Issue Section:
Technical Papers
1.
Sue
, H. J.
, Huang
, J.
, and Yee
, A. F.
, 1992
, “Interfacial Adhesion and Toughening Mechanisms in an Alloy of Polycarbonate/Polyethylene
,” Polymer
, 33
, No. 22
, pp. 4868
–4871
.2.
Collias
, D. I.
, Baird
, D. G.
, and Borggreve
, R. J. M.
, 1994
, “Impact Toughening of Polycarbonate by Microcellular Foaming
,” Polymer
, 35
, No. 18
, pp. 3978
–3983
.3.
Seeler
, K. A.
, and Kumar
, V.
, 1995
, “Decoupling the Effects of the Matrix Properties and Foam Structure on the Mechanical Properties of Microcellular Foam by Sub-Tg Annealing
,” J. Reinf. Plast. Compos.
, 14
, pp. 1054
–1068
.4.
Kumar
, V.
, and Weller
, J. E.
, 1994
, “Production of Microcellular Polycarbonate Using Carbon Dioxide for Bubble Nucleation
,” ASME J. Ind.
, 116
, pp. 413
–421
.5.
Weller, J. E., 1996, “
The Effects of Processing and Microstructure on the Tensile Behavior of Microcellular Foams,” Ph.D. thesis, Dept. of Mechanical Engineering, University of Washington, Seattle.
6.
Holl
, M.
, 1994
, “The University of Washington Saturation Vessel Pressure and Temperature Control System
,” Cellular Composites Consortium Report
#8
, University of Washington, Seattle, WA.
7.
Annual Book of ASTM Standards, 1996, Vol. 8.01, American Society for Testing and Materials, Philadelphia, PA, pp. 1–18, 293–296.
8.
Underwood, E. E., 1970, Quantitative Stereology, Addison-Wesley, Reading, MA.
9.
Wu
, S.
, 1987
, “A Generalized Criterion for Rubber Toughening: The Critical Matrix Ligament Thickness
,” Polym. Prepr. (Am. Chem. Soc. Div. Polym. Chem.)
, 28
, No. 2
, pp. 179
–80
.10.
van der Sanden
, M. C. M.
, Meijer
, H. E. H.
, and Lemstra
, P. J.
, 1993
, “Deformation and Toughness of Polymeric Systems: 1. The Concept of a Critical Thickness
,” Polymer
, 34
, No. 10
, pp. 2948
–2154
.11.
van der Sanden
, M. C. M.
, Meijer
, H. E. H.
, and Tervoort
, T. A.
, 1993
, “Deformation and Toughness of Polymeric Systems: 2. Influence of Entanglement Density
,” Polymer
, 34
, No. 14
, pp. 2961
–2170
.Copyright © 2001
by ASME
You do not currently have access to this content.