As additive manufacturing (AM) technologies utilizing metal powders continue to mature, the usage of AM parts in gas turbine engines will increase. Current metal AM technologies produce parts with substantial surface roughness that can only be removed from external surfaces and internal surfaces that are accessible for smoothing. Difficulties arise in making smooth the surfaces of small internal channels, which means the augmentation of pressure loss and heat transfer due to roughness must be accounted for in the design. As gas turbine manufacturers have only recently adopted metal AM technologies, much remains to be examined before the full impacts of applying AM to turbine parts are understood. Although discrete film cooling holes have been extensively studied for decades, this objective of this study was to understand how the roughness of film cooling holes made using AM can affect the overall cooling effectiveness. Coupons made from a high temperature nickel alloy with engine-scale film holes were tested in a rig designed to simulate engine relevant conditions. Two different hole sizes and two different build directions were examined at various blowing ratios. Results showed that the effectiveness is dependent on the build direction and the relative size of the hole. It was also discovered that commercially available AM processes could not reliably produce small holes with predictable behavior.
Effectiveness Measurements of Additively Manufactured Film Cooling Holes
Contributed by the International Gas Turbine Institute (IGTI) of ASME for publication in the JOURNAL OF TURBOMACHINERY. Manuscript received September 14, 2017; final manuscript received October 3, 2017; published online October 31, 2017. Editor: Kenneth Hall.
Stimpson, C. K., Snyder, J. C., Thole, K. A., and Mongillo, D. (October 31, 2017). "Effectiveness Measurements of Additively Manufactured Film Cooling Holes." ASME. J. Turbomach. January 2018; 140(1): 011009. https://doi.org/10.1115/1.4038182
Download citation file: